JOURNAL OF THERMAL ANALYSIS AND CALORIMETRY
卷 138, 期 6, 页码 4395-4405出版社
SPRINGER
DOI: 10.1007/s10973-019-08881-7
关键词
Thermal analysis; DSC; TG; DMA; Halogenated butyl rubber; Curing agents
资金
- Young Scientists' Fund at the Faculty of Chemistry, Lodz University of Technology [W-3D/FMN/34G/2016]
The aim of this work was to examine the influence of new curing agents proposed for brominated butyl rubber (BIIR) on the cross-linking process of rubber compounds and the thermal behavior of the vulcanizates. Rubber blends that were filled with carbon black and contained acetylacetonates of different transition metals in the presence of triethanolamine (TEOA) as new cross-linking agents were prepared. The performed studies showed that metal acetylacetonates (Me(acac)) are effective cross-linking agents for BIIR, which was confirmed by high values of the torque increment ( increment M) and significant cross-linking degree of the vulcanizates (alpha((T))). The most active curing agent seems to be iron acetylacetonate (Fe(acac)). Its application results in a shorter optimal vulcanization time, lower onset vulcanization temperature and similar vulcanization enthalpy compared to the BIIR cured with a sulfur curing system. The BIIR vulcanizates cured with Me(acac) reveal good mechanical properties with tensile strengths in the range of 9-14 MPa and better damping properties comparing to the sulfur-cured rubber. The proposed curing agents do not significantly affect the thermal stability of the BIIR vulcanizates.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据