JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS
卷 490, 期 -, 页码 -出版社
ELSEVIER
DOI: 10.1016/j.jmmm.2019.165454
关键词
La/Ce doping; Rapid quenching; NdFeB-based alloys; Phase structure; Magnetic properties
资金
- National Key Research and Development Program [2016YFB0700902]
Investigation of the phase structure of [Nd1-x(LayCe1-y)(x)](2)Fe14B (x = 0-0.7, y = 0, 0.2, 0.4, 0.5, 0.6, 0.8, 1.0) melt spun ribbons and their magnetic properties is presented. The La-Ce co-doped Nd-Fe-B alloys are compared with the La doping and Ce doping respectively by controlling the doping ratio of La/Ce. It can be found that the Nd-Fe-B alloys remain single 2:14:1 phase with Ce doping. In contrast, the 2:14:1 phase begins to decompose when the doping content of La reaches 30at.%. The 2:14:1 phase decomposes seriously with the La doping content over 50at.%, accompanied by the rising of secondary phases. The magnetic properties of Nd-Fe-B alloy decrease with the increasing of La, Ce doping content. The performance of La-doped Nd-Fe-B is superior to that of Ce-doped when the addition of La is less than 50at.%. However, severe phase decomposition of 2:14:1 phase with x more than 0.5 leads to the sharp decline of magnetic properties of La-doped Nd-Fe-B. In general, the magnetic properties, especially for the B-r and (BH)(max) of La-Ce co-doped Nd-Fe-B are better than single-doped cases. And the co-doped Nd-Fe-B alloys show greater enhancement of (BH)(max) with the increasing amount of total doping content. For example, when the total doping concentration reaches 50at.%, the (BH)(max) of [Nd-0(.5)(La0.6Ce0.4)(0)(.5)](2)Fe14B still reaches 12.4MGOe, which is much higher than (Nd0.5Ce0.5)(2)Fe14B ((BH)(max) = 8.2MGOe).
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据