期刊
COMPOSITES PART B-ENGINEERING
卷 172, 期 -, 页码 54-60出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.compositesb.2019.05.067
关键词
Ti-6A1-4V alloy; In situ composite; Friction stir processing; Compressive test; Nanoindentation
资金
- Army Research Laboratory [W911NF-18-2-0067]
- University of North Texas [W911NF-18-2-0067]
In situ titanium matrix composites were fabricated by introducing an exothermic reaction between Ti and B4C during friction stir processing (FSP). Formation of TiB, TiB2, and TiC was confirmed by X-ray diffraction and transmission electron microscopy along with energy dispersive X-ray spectroscopy and diffraction pattern. TiB and TiB2 whiskers and TiC particles influenced the dynamic recrystallization process, which facilitated an equiaxed grained structure rather than the Widmanstatten microstructure. Mechanical properties of as-received Ti-6A1-4V including hardness, elastic modulus, compressive yield strength and work-hardening rate (stage B) were improved by similar to 57%, 17%, 47% and 100%, respectively, after FSP with B4C.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据