CEMENT AND CONCRETE RESEARCH
卷 123, 期 -, 页码 -出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.cemconres.2019.05.018
关键词
High temperature; Portland cement; GGBFS; Microstructure; C-S -H
资金
- National Natural Science Foundation of China [51778132]
- 973 program [2015CB655100]
- MOST, China
This investigation focuses on the change of C-S-H gels in Portland cement (PC) paste and PC/ground granulated blast-furnace slag (GGBFS) blended paste at elevated temperature up to 800 degrees C. Spark-like phase, which might be spurrite, can be found in the inner product of C3S in PC paste when the temperature is higher than 600 degrees C. The gels in PC paste show an obvious change in composition in comparison with the gels in GGBFS blended paste at elevated temperature. After 600 degrees C, the continuous decomposition and shrinkage of C-S-H gels results in the increase of small pores (10-40 nm) in both pastes. The nitrogen adsorption results show that some gels, which should be C-A-S-H in GGBFS blended paste, are quite stable at high temperature. The results of this study provide a comprehensive understanding of the different behavior between gels in PC paste and GGBFS blended paste at high temperature.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据