Preparation of crosslinked polysiloxane/SiO2 nanocomposite via in-situ condensation and its surface modification on cotton fabrics

Novel crosslinked polysiloxane/SiO2 nanocomposite (CLPS-SiO2) was successfully prepared via the in situ condensation reaction of silica sols and crosslinked polysiloxane with end-capped triethoxysilane in solvent, which was firstly fabricated through the modification of our previously developed crosslinked polysiloxane with end-capped epoxy groups using aminopropyltriethoxysilane (APTES) and noted as APTES-CLPS. Chemical structures and thermal properties of the as-prepared resultants were characterized by Fourier transform infrared spectroscopy (FTIR), nuclear magnetic resonance spectra (H-1/C-13 NMR) and thermogravimetric analysis (TGA). CLPS-SiO2 was applied as surface modification agent to treat cotton fabrics. Film morphologies and surface properties were examined with scanning electron microscopy (SEM), atomic force microscopy (AFM), X-ray photoelectron spectroscopy (XPS), contact angle measurements, and other instruments. FTIR and NMR confirmed structure of the products. CLPS-SiO2 showed better thermal stability than APTES-CLPS due to anchor of the nanosilica. APTES-CLPS could deposit a smooth film on cotton fiber surface. Besides, CLPS-SiO2 also coated the fibers with many nano-scaled tubercles beneath this smooth film by SEM. However, the APTES-CLPS film and the CLPS-SiO2 film on silicon-wafer were never homogeneous and had a few low or high peaks. The root mean square roughness (Rq) of APTES-CLPS film reached to 0.441 nm in 2 x 2 mu m(2) scanning field and at 5 nm data scale. Owing to the incorporation of nanosilica, that of CLPS-SiO2 film continuously increased and could attain 4.528 nm in 2 x 2 mu m(2) scanning field and at 20 nm data scale. XPS analysis further demonstrates that there was a CLPS-SiO2 film covered on the cotton surface and the silyl groups had the tendency to enrich at the film-air interface. In addition, hydrophobicity of the CLPS-SiO2 treated fabric would be enhanced with augment of the amount of nanocomposite. Water contact angle of this fabric could finally attain 158.0. But most of all, its color and softness would not be influenced instead. The CLPS-SiO2 treated fabric possessed good washing durability. (C) 2016 Elsevier B.V. All rights reserved.