Diesel engine; Selective catalytic reduction; Durability test; NOx emissions; Catalyst characterization
资金
- National Key R&D Program of China [2017YFC0211202]
- National High Technology Research and Development Program of China [2012AA111720]
The durability of V2O5-WO3/TiO2 selective catalytic reduction (SCR) catalysts for heavy-duty diesel engines was evaluated based on 500 h SCR durability tests conducted using B20 fuel (20% v/v biodiesel + 80% v/v petroleum diesel). The fresh and deteriorated SCR catalysts were characterized by Xray fluorescence, X-ray diffraction, and Brunauer-Emmett-Teller surface area measurements to investigate the deterioration mechanism of the catalysts. The results show that the SCR de-NOx performance is degraded after SCR durability testing, particularly at high engine speeds. The NOx conversion efficiency of the deteriorated SCR catalysts decreases at temperatures above 400 degrees C but remains high at temperatures between 250 and 400 degrees C. The catalyst characterization results reveal that the deterioration in the de-NOx performance is not owing to anatase-to-rutile transformation of TiO2, but because of a decrease in the specific surface area and the loss of the catalyst components, which are greater in the front cross section of the SCR than in the rear cross section. For a given catalyst cross section, the decrease in the specific surface area exhibits a positive correlation with the flow rate of the exhaust gas. (C) 2019 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据