Effects of Different Parameters on Initiation and Propagation of Stress Corrosion Cracks in Pipeline Steels: A Review
出版年份 2019 全文链接
标题
Effects of Different Parameters on Initiation and Propagation of Stress Corrosion Cracks in Pipeline Steels: A Review
作者
关键词
-
出版物
Metals
Volume 9, Issue 5, Pages 590
出版商
MDPI AG
发表日期
2019-05-23
DOI
10.3390/met9050590
参考文献
相关参考文献
注意:仅列出部分参考文献,下载原文获取全部文献信息。- Important Factors on the Failure of Pipeline Steels with Focus on Hydrogen Induced Cracks and Improvement of Their Resistance: Review Paper
- (2019) M. A. Mohtadi-Bonab et al. METALS AND MATERIALS INTERNATIONAL
- Role of cold rolled followed by annealing on improvement of hydrogen induced cracking resistance in pipeline steel
- (2018) M.A. Mohtadi-Bonab et al. ENGINEERING FAILURE ANALYSIS
- Hydrogen induced cracking of pipeline and pressure vessel steels: A review
- (2018) Goutam Ghosh et al. ENGINEERING FRACTURE MECHANICS
- Microstructural aspects of intergranular and transgranular crack propagation in an API X65 steel pipeline related to fatigue failure
- (2018) M.A. Mohtadi-Bonab et al. ENGINEERING FAILURE ANALYSIS
- Influence of inclusions on initiation of pitting corrosion and stress corrosion cracking of X70 steel in near-neutral pH environment
- (2018) Liwei Wang et al. CORROSION SCIENCE
- A focus on different factors affecting hydrogen induced cracking in oil and natural gas pipeline steel
- (2017) M.A. Mohtadi-Bonab et al. ENGINEERING FAILURE ANALYSIS
- Comparative study on the stress corrosion cracking of X70 pipeline steel in simulated shallow and deep sea environments
- (2017) Feilong Sun et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Effect of different microstructural parameters on hydrogen induced cracking in an API X70 pipeline steel
- (2017) M. A. Mohtadi-Bonab et al. METALS AND MATERIALS INTERNATIONAL
- Effect of alternating current on stress corrosion cracking behavior and mechanism of X80 pipeline steel in near-neutral solution
- (2017) Hongxia Wan et al. Journal of Natural Gas Science and Engineering
- Effect of Cu Addition in Pipeline Steels on Prevention of Hydrogen Permeation in Mildly Sour Environments
- (2016) Kazuhiko Baba et al. CORROSION
- EIS analysis on stress corrosion initiation of pipeline steel under disbonded coating in near-neutral pH simulated soil electrolyte
- (2016) Y.A.N. Maocheng et al. CORROSION SCIENCE
- A New Understanding on AC Corrosion of Pipeline Steel in Alkaline Environment
- (2016) M. Zhu et al. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE
- Effect of Microstructural Parameters on Fatigue Crack Propagation in an API X65 Pipeline Steel
- (2016) M. A. Mohtadi-Bonab et al. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE
- Effect of arisen dislocation density and texture components during cold rolling and annealing treatments on hydrogen induced cracking susceptibility in pipeline steel
- (2016) M.A. Mohtadi-Bonab et al. JOURNAL OF MATERIALS RESEARCH
- Investigation of hydrogen assisted cracking in acicular ferrite using site-specific micro-fracture tests
- (2016) Walter L. Costin et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Effect of hydrogen-induced plasticity on the stress corrosion cracking of X70 pipeline steel in simulated soil environments
- (2016) Z.Y. Liu et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Effect of Cu Addition in Pipeline Steels on Prevention of Hydrogen Permeation in Mildly Sour Environments
- (2016) Kazuhiko Baba et al. CORROSION
- Novel Cu-bearing high-strength pipeline steels with excellent resistance to hydrogen-induced cracking
- (2016) Xianbo Shi et al. MATERIALS & DESIGN
- Industrial products and wastes as adsorbents for sulphate and chloride removal from synthetic alkaline solution and mine process water
- (2015) Evgenia Iakovleva et al. CHEMICAL ENGINEERING JOURNAL
- The mechanism of failure by hydrogen induced cracking in an acidic environment for API 5L X70 pipeline steel
- (2015) M.A. Mohtadi-Bonab et al. INTERNATIONAL JOURNAL OF HYDROGEN ENERGY
- Effect of Microstructure on Hydrogen Induced Cracking Behavior of a High Deformability Pipeline Steel
- (2015) Xian-bo SHI et al. JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL
- HIC and SSC Behavior of High-Strength Pipeline Steels
- (2015) Xian-Bo Shi et al. Acta Metallurgica Sinica-English Letters
- Effect of AC on stress corrosion cracking behavior and mechanism of X80 pipeline steel in carbonate/bicarbonate solution
- (2014) Min Zhu et al. CORROSION SCIENCE
- Effect of electrolyte composition on crack growth rate in pipeline steel
- (2014) A.I. Marshakov et al. CORROSION SCIENCE
- The generation of corrosion under insulation and stress corrosion cracking due to sulphide stress cracking in an austenitic stainless steel hydrocarbon gas pipeline
- (2014) P. Roffey et al. ENGINEERING FAILURE ANALYSIS
- Effect of Strength and Microstructure on Stress Corrosion Cracking Behavior and Mechanism of X80 Pipeline Steel in High pH Carbonate/Bicarbonate Solution
- (2014) Min Zhu et al. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE
- Study of the failure mechanism of an epoxy coating system under high hydrostatic pressure
- (2013) Ying Liu et al. CORROSION SCIENCE
- New findings on the factors accelerating AC corrosion of buried pipeline
- (2013) Zitao Jiang et al. CORROSION SCIENCE
- Effect of AC current density on stress corrosion cracking behavior of X80 pipeline steel in high pH carbonate/bicarbonate solution
- (2013) Min Zhu et al. ELECTROCHIMICA ACTA
- A comparative study of hydrogen induced cracking behavior in API 5L X60 and X70 pipeline steels
- (2013) M.A. Mohtadi-Bonab et al. ENGINEERING FAILURE ANALYSIS
- Electrochemical impedance spectroscopy analysis of X70 pipeline steel stress corrosion cracking in high pH carbonate solution
- (2012) A.A. Oskuie et al. CORROSION SCIENCE
- Evaluation of environment-assisted cracking susceptibility of a grade X100 pipeline steel
- (2011) A. Mustapha et al. CORROSION SCIENCE
- Stress Corrosion Cracking of X80 Pipeline Steel in Near-Neutral pH Environment under Constant Load Tests with and without Preload
- (2011) Y.Z. Jia et al. JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
- Effect of bainitic microstructure on the susceptibility of pipeline steels to hydrogen induced cracking
- (2011) M.A. Arafin et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Effects of alternating and direct current in electrocoagulation process on the removal of cadmium from water – A novel approach
- (2011) Subramanyan Vasudevan et al. SEPARATION AND PURIFICATION TECHNOLOGY
- Environmentally assisted cracking mechanism of pipeline steel in near-neutral pH groundwater
- (2010) B.T. Lu et al. CORROSION SCIENCE
- Simulation of crack growth during hydrostatic testing of pipeline steel in near-neutral pH environment
- (2010) Yongwang Kang et al. CORROSION SCIENCE
- Transgranular crack growth in the pipeline steels exposed to near-neutral pH soil aqueous solutions: The role of hydrogen
- (2009) W. Chen et al. ACTA MATERIALIA
- Effect of inclusions on initiation of stress corrosion cracks in X70 pipeline steel in an acidic soil environment
- (2009) Z.Y. Liu et al. CORROSION SCIENCE
- Metallurgical factors in stress corrosion cracking (SCC) and hydrogen-induced cracking (HIC)
- (2009) M. Elboujdaini et al. JOURNAL OF SOLID STATE ELECTROCHEMISTRY
- Effects of dissolved hydrogen and elastic and plastic deformation on active dissolution of pipeline steel in anaerobic groundwater of near-neutral pH
- (2008) B.T. Lu et al. ACTA MATERIALIA
- Effect of environmental and metallurgical factors on hydrogen induced cracking of HSLA steels
- (2008) Wan Keun Kim et al. CORROSION SCIENCE
- A new understanding of intergranular stress corrosion cracking resistance of pipeline steel through grain boundary character and crystallographic texture studies
- (2008) M.A. Arafin et al. CORROSION SCIENCE
Discover Peeref hubs
Discuss science. Find collaborators. Network.
Join a conversationFind the ideal target journal for your manuscript
Explore over 38,000 international journals covering a vast array of academic fields.
Search