Mode I Interlaminar Fracture of Glass/Epoxy Unidirectional Laminates. Part I: Experimental Studies
出版年份 2019 全文链接
标题
Mode I Interlaminar Fracture of Glass/Epoxy Unidirectional Laminates. Part I: Experimental Studies
作者
关键词
-
出版物
Materials
Volume 12, Issue 10, Pages 1607
出版商
MDPI AG
发表日期
2019-05-16
DOI
10.3390/ma12101607
参考文献
相关参考文献
注意:仅列出部分参考文献,下载原文获取全部文献信息。- Experimental method for mode I fracture toughness of composite laminates using wedge loaded double cantilever beam specimens
- (2018) Sota Oshima et al. COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING
- Clustering of interlaminar and intralaminar damages in laminated composites under indentation loading using Acoustic Emission
- (2018) Milad Saeedifar et al. COMPOSITES PART B-ENGINEERING
- Barely visible impact damage assessment in laminated composites using acoustic emission
- (2018) Milad Saeedifar et al. COMPOSITES PART B-ENGINEERING
- Loading rate dependency of Mode I interlaminar fracture toughness for unidirectional composite laminates
- (2018) Huifang Liu et al. COMPOSITES SCIENCE AND TECHNOLOGY
- Barely visible impact damages of GFRP laminate profiles – An experimental study
- (2018) Adrian Gliszczynski et al. COMPOSITES PART B-ENGINEERING
- Numerical analysis of the DCB test configuration applicability to mechanically coupled Fiber Reinforced Laminated Composite beams
- (2016) Sylwester Samborski COMPOSITE STRUCTURES
- Experimental investigation of failure process in compressed channel-section GFRP laminate columns assisted with the acoustic emission method
- (2015) Tomasz Kubiak et al. COMPOSITE STRUCTURES
- Loading rate dependency on mode I interlaminar fracture toughness of unidirectional and woven carbon fibre epoxy composites
- (2015) H. Zabala et al. COMPOSITE STRUCTURES
- Mode-I, mode-II and mixed-mode I+II fracture behavior of composite bonded joints: Experimental characterization and numerical simulation
- (2015) I.S. Floros et al. COMPOSITES PART B-ENGINEERING
- Measuring the delamination length in static and fatigue mode I tests using video image processing
- (2014) F. Lahuerta et al. COMPOSITES PART B-ENGINEERING
- Influence of autoclaving process parameters on the buckling and postbuckling behaviour of thin-walled channel section beams
- (2014) Jaroslaw Bienias et al. THIN-WALLED STRUCTURES
- Comparison of intralaminar and interlaminar mode I fracture toughnesses of a unidirectional IM7/8552 carbon/epoxy composite
- (2013) Michael W. Czabaj et al. COMPOSITES SCIENCE AND TECHNOLOGY
- Quantitative experimental measurements of matrix cracking and delamination using acoustic emission
- (2010) Jonathan J. Scholey et al. COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING
- Ultimate Strength Prediction of Carbon/Epoxy Tensile Specimens from Acoustic Emission Data
- (2010) V. Arumugam et al. JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
- An integrated approach based on acoustic emission and mechanical information to evaluate the delamination fracture toughness at mode I in composite laminate
- (2010) A. Refahi Oskouei et al. MATERIALS & DESIGN
- Interlaminar and intralaminar fracture characterization of composites under mode I loading
- (2009) M.F.S.F. de Moura et al. COMPOSITE STRUCTURES
- A procedure for superposing linear cohesive laws to represent multiple damage mechanisms in the fracture of composites
- (2009) Carlos G. Dávila et al. INTERNATIONAL JOURNAL OF FRACTURE
- Detection of delamination defects in CFRP materials using ultrasonic signal processing
- (2008) Abdessalem Benammar et al. ULTRASONICS
- Equivalent crack based analyses of ENF and ELS tests
- (2007) M.F.S.F. de Moura et al. ENGINEERING FRACTURE MECHANICS
Create your own webinar
Interested in hosting your own webinar? Check the schedule and propose your idea to the Peeref Content Team.
Create NowAsk a Question. Answer a Question.
Quickly pose questions to the entire community. Debate answers and get clarity on the most important issues facing researchers.
Get Started