WEAR
卷 426, 期 -, 页码 357-369出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.wear.2018.11.032
关键词
Cold spray; Metal matrix composites; Sliding wear; Ti6Al4V; Tribo-oxides
资金
- Natural Science and Engineering Research Council (NSERC) Strategic Grants Program
The poor wear resistance of titanium and its alloys often results in galling and high wear rates. One method to improve their wear resistance is by hard secondary phase reinforcement to create a metal matrix composite, which can be utilized in the bulk or as a coating. In the present study, Ti6Al4V coatings and Ti6Al4V-TiC metal matrix composite coatings were deposited on mild steel substrates using cold spray process and their dry sliding wear behavior was studied over a static temperature range of 25-575 degrees C. Tests were performed using a unidirectional ball-on-disc tribometer with WC-Co sphere as the counterface at a load of 2.5 N and sliding velocity of 2.1 cm s(-1). Wear rate and coefficient of friction (CoF) decreased with an increase in temperature and composite coatings exhibited higher wear resistance at all temperatures. Below 200 degrees C, abrasive wear characterized by ploughing by wear debris resulted in high wear of Ti6Al4V coatings, whereas formation of tribolayers led to lower wear of composite coatings. At elevated temperatures ( > 200 degrees C), oxide glaze layers formed on both coatings were composed of WO3, TiO2 and CoWO4. Electron channel contrast imaging of the wear track cross-sections showed no splat debonding, less extent of recrystallization and larger grain sizes (at 575 degrees C) in composite coatings compared to Ti6Al4V.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据