Synthesis of hard magnetic NdFeB composite particles by recycling the waste using microwave assisted auto-combustion and reduction method

The present work provides a facile and energy-saving approach to recycle Nd-Fe-B wastes. Employing the severely oxidized and contaminated sintered Nd-Fe-B scraps as the raw materials, sub-micro sized Nd-Fe-B/alpha-Fe composite magnetic powders were successfully synthesized by microwave assisted autocombustion method followed by a reduction diffusion process. In details, the waste magnets were dissolved in HNO3 solution and both the rare earth oxides and iron oxide were obtained by autocombustion approach with the help of microwave heating. These oxides were then reduced to achieve Nd-Fe-B alloys with the reducing agent CaH2.To modify the composition of the final product, Nd (NO3)(3)center dot 6H(2)O and H3BO3 were added during dissolving and consequently three compositions of the final products were obtained. TEM results demonstrate that the sizes of alpha-Fe and Nd2Fe14B grains are below 10 nm and 20 nm, respectively. The magnetic properties of the composite powders obtained from the wastes in this study are comparable to those obtained by other methods using pure reagents. The room temperature coercivity of as-synthesized Nd15Fe77B8 is higher than 400 kA/m. In addition, an appropriate mass ratio of CaH2 to Nd-Fe-B oxides is required in order to obtain good magnetic properties. (C) 2019 Elsevier Ltd. All rights reserved.