CeO2/ZnO nano-composite; p-Nitrophenol; Sensing; Photocatalytic
资金
- UGC-New Delhi under UGC SAP of the Chemistry Department, H.P. University Shimla
- UGC
- UGC New Delhi
CeO2/ZnO nano-composite was synthesized via solution combustion synthesis (SCS) and annealed at 500 degrees C. As synthesized material was characterized in terms of field emission scanning electron microscopy (FE-SEM), energy dispersive spectroscopy (EDS), powdered X-ray diffraction (PXRD), fourier transform-infrared spectroscopy (FT-IR) and UV-visible spectroscopy. The surface properties of as-synthesized nano-composite were obtained from N-2 gas BET analysis. FESEM and XRD results indicate that as-synthesized material composed of two different morphologies, i.e. distinctly distinct hexagonal nanorods and aggregated spherical-shaped nanoparticles of CeO2/ZnO nano-composite. The nanorods were estimated to be 500 50 am in length and 90-140 nm in diameter. From the photocatalytic degradation of PNP, 0.15 g of CeO2/ZnO was found to be the optimum amount for the maximum degradation p-nitrophenol (PNP) molecules in 200 min. Chemical sensing study indicated that the material was highly selective to PNP with a theoretical detection limit of 3.05 pM L-1, which is believed to be due to the formation of new sites relatively more compatible to the adsorption of PNP.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据