MATERIALS CHARACTERIZATION
卷 149, 期 -, 页码 218-225出版社
ELSEVIER SCIENCE INC
DOI: 10.1016/j.matchar.2019.01.035
关键词
Transmission electron microscopy (TEM); Al-Mg-Si alloy; Precipitate crystal structure; Heat exchangers
类别
资金
- AMPERE project a Knowledge building Project for Industry - Research Council of Norway (RCN) [247783]
- Norsk Hydro
- Sapa
- Granges
- Neuman Aluminium Raufoss (Raufoss Technology)
- Nexans
- RCN
- UNINETT Sigma2 - the National Infrastructure for High Performance Computing and Data Storage in Norway [nn9128k]
During manufacturing of heat exchangers, the core material is cladded with a lower-melting point alloy, rolled into thin strips before being formed and finally brazed at an elevated temperature. After a period of natural aging, the final product is operated at two different temperatures depending on the application: about 95 degrees C for radiators, and peaks up to about 250 degrees C for charge-air-coolers. For an Al-Mg-Si-Cu alloy type core material, this process translates into solution heat treatment, natural aging and aging during operation. High-resolution imaging with aberration corrected high angle annular dark field scanning transmission electron microscopy (HAADF-STEM) revealed the presence of a complex mix of precipitates after 58 days at 95 degrees C, including a never before-reported phase which structurally is a mix between Al-Cu and Al-Mg-Si type precipitates. The stability of this phase is investigated with density functional theory (DFT). Q' is the main phase observed after 5 h at 250 degrees C, with most precipitates incorporating a certain type of stacking fault.