期刊
ACS APPLIED MATERIALS & INTERFACES
卷 10, 期 44, 页码 38294-38301出版社
AMER CHEMICAL SOC
DOI: 10.1021/acsami.8b13550
关键词
TPD-based polymer; organic photodetector; organic photodiode; low dark current; high responsivity
资金
- National Research Council of Science & Technology (NST) by Korea government (MSIT) (GCRC SOP) [CAP - 15 - 04 - KITECH, NRF-2017R1A2A2A05001345, 2011-0030013]
Organic photodetectors (OPDs) are attracting attention for use in flexible and portable electronic applications such as image sensors, remote sensing, optical communications, and medical sensors because of their strong photon responsivity in thin films over a broad range of wavelengths. In particular, the efficient photon-to-current conversion of OPDs under visible light allows their use in indirect X-ray detectors using scintillators to convert X-rays to visible light. The polymer poly(4,8-bis(5-(2-ethylhexyl)thiophen-2-yl)benzo[1,2-b:4,5-b']-dithiophene-co-5-(2-hexyldecy1)-1,3-bis(6-octylthieno [3,2-b]thiophen-2-yl)-4H-thieno [3,4-c]pyrrole-4,6(5H)-dione) (PBDTT-8ttTPD) shows strong absorption bands in the region of 500-650 nm, as well as high hole mobility, which provides excellent photoresponsivity and photon-to current conversion efficiency. A p-n junction photodetector was fabricated by blending PBDTT-8ttTPD and [6,6]-phenyl C-71 butyric acid methyl ester (PC71BM) and varying the thickness of the active layer (260-1100 nm). The PBDTT-8ttTPD:PC71BM-based OPDs show promising photodetecting properties having a low dark current of 3.72 x 10(-9) A cm(-2) and high responsivity of 0.39 A W-1 because of the well-controlled morphology, high molar absorption coefficient, and excellent carrier mobility of the PBDTT-8ttTPD:PC71BM layer. Consequently, the specific detectivity of the PBDTT-8ttTPD-based OPD devices was 1.13 x 10(13) Jones at -2 V on irradiation with a light-emitting diode (530 nm wavelength) with a power density of 55.6 mu W cm(-2).
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据