MATERIALS & DESIGN
卷 84, 期 -, 页码 378-384出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.matdes.2015.06.160
关键词
Titanium aluminide; Fatigue lifetime; Stress ratio; Cyclic creep; In situ observation
资金
- National Key Basic Research Program (973) [2011CB605506]
- National Natural Science Foundation of China [21171018, 51271021]
The effect of stress ratio (R) on fatigue lifetime of a cast Ti-45Al-8.0Nb-0.2W-0.2B-0.1Y (at.%) alloy was investigated at 750 degrees C. Fatigue tests with various stress ratios ranging from 0.1 to 1 were performed using a mini servo-hydraulic fatigue machine inside a chamber of scanning electron microscope (SEM). Fatigue crack initiation and propagation behavior was studied by in situ SEM observation and fatigue fracture mode was examined by fracture surface analysis. It is found that fatigue lifetime shows a reversed S-type curve with the increase of stress ratio. At R ranging from 0.1 to 0.4, creep-fatigue interaction dominates the fatigue lifetime and the fatigue lifetime reaches its minimum value at R = 0.3. At R ranging from 0.4 to 1, creep damage dominates the fatigue lifetime and the fatigue lifetime exhibits inverse proportional relation with R. Meanwhile, with the increase of stress ratio, the fatigue crack initiation sites transform from lamellar interface at R=0.1, to lamellar interface and colony boundary at R = 0.3, and to lamellar colony boundary at R = 0.5. Accordingly, the fatigue fracture mode transforms from transgranular cracking, to transgranular and intergranular cracking, and to intergranular cracking. (C) 2015 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据