期刊
JOURNAL OF ADVANCED CERAMICS
卷 2, 期 1, 页码 55-62出版社
TSINGHUA UNIV PRESS
DOI: 10.1007/s40145-013-0042-4
关键词
YSZ; films; LSM; sol-gel; dip-coating
资金
- CAPES
Yttria-stabilized zirconia (YSZ, ZrO2-8% Y2O3) films were deposited onto lanthanum strontium manganite (LSM, La0.7Sr0.3MnO3) substrates using dip-coating process aiming for the application in solid oxide fuel cells (SOFCs). YSZ precursor was prepared by sol-gel method; three values of the organic/inorganic concentration ratio (1, 3 and 5) were utilized and the sol viscosity was adjusted (60 mPa.s and 100 mPa.s) before deposition on the substrate. The influence of these synthesis parameters on the structure and morphology of the deposited films was examined by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The films showed characteristic peaks of LSM, YSZ (with cubic structure) and secondary phases of SrZrO3 and La2O3. Depending on the synthesis conditions, crack-free, homogeneous and well adhered films were obtained, with thickness of 11-24 mu m.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据