期刊
ACTA CRYSTALLOGRAPHICA SECTION B-STRUCTURAL SCIENCE CRYSTAL ENGINEERING AND MATERIALS
卷 70, 期 -, 页码 828-838出版社
INT UNION CRYSTALLOGRAPHY
DOI: 10.1107/S2052520614013687
关键词
-
In surficial environments, the fate of many elements is influenced by their interactions with the phyllomanganate vernadite, a nano-sized and turbostratic variety of birnessite. To advance our understanding of the surface reactivity of vernadite as a function of pH, synthetic vernadite (delta-MnO2) was equilibrated at pH ranging from 3 to 10 and characterized structurally using chemical methods, thermogravimetry and modelling of powder X-ray diffraction (XRD) patterns. With decreasing pH, the number of vacant layer sites increases in the octahedral layers of delta-MnO2 (from 0.14 per layer octahedron at pH 10 to 0.17 at pH 3), whereas the number of layer Mn3+ is, within errors, equal to 0.12 per layer octahedron over the whole pH range. Vacant layer sites are capped by interlayer Mn3+ sorbed as triple corner-sharing surface complexes (TC sites). The increasing number of interlayer Mn3+ with decreasing pH (from 0.075 per layer octahedron at pH 10 to 0.175 at pH 3) results in the decrease of the average Mn oxidation degree (from 3.80 +/- 0.01 at pH 10 to 3.70 +/- 0.01 at pH 3) and in the lowering of the Na/Mn ratio (from 27.66 +/- 0.20 at pH 10 to 6.99 +/- 0.16 at pH 3). In addition, in-plane unit-cell parameters are negatively correlated to the number of interlayer Mn at TC sites and decrease with decreasing pH (from b = 2.842 angstrom at pH 10 to b = 2.834 angstrom at pH 3), layer symmetry being systematically hexagonal with a = b x 3(1/2). Finally, modelling of X-ray diffraction (XRD) patterns indicates that crystallite size in the ab plane and along the c* axis decreases with decreasing pH, ranging respectively from 7 nm to 6 nm, and from 1.2 nm to 1.0 nm (pH 10 and 3, respectively). Following their characterization, dry samples were sealed in polystyrene vials, kept in the dark, and reanalysed 4 and 8 years later. With ageing time and despite the dry state, layer Mn3+ extensively migrates to the interlayer most likely to minimize steric strains resulting from the Jahn-Teller distortion of Mn3+ octahedra. When the number of interlayer Mn3+ at TC sites resulting from this migration reaches the maximum value of similar to 1/3 per layer octahedron, interlayer species from adjacent layers share their coordination sphere, resulting in cryptomelane-like tunnel structure fragments (with a 2 x 2 tunnel size) with a significantly improved layer stacking order.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据