Accelerated Stress Tests of Pt/HSAC Electrocatalysts: an Identical-Location Transmission Electron Microscopy Study on the Influence of Intermediate Characterizations
出版年份 2013 全文链接
标题
Accelerated Stress Tests of Pt/HSAC Electrocatalysts: an Identical-Location Transmission Electron Microscopy Study on the Influence of Intermediate Characterizations
作者
关键词
Proton exchange membrane fuel cells, Carbon-supported Pt nanoparticles, Electrocatalysts degradation mechanisms, Identical-location transmission electron microscopy, Intermediate characterizations
出版物
Electrocatalysis
Volume 5, Issue 2, Pages 125-135
出版商
Springer Nature
发表日期
2013-11-21
DOI
10.1007/s12678-013-0173-y
参考文献
相关参考文献
注意:仅列出部分参考文献,下载原文获取全部文献信息。- Probing the structure, the composition and the ORR activity of Pt3Co/C nanocrystallites during a 3422h PEMFC ageing test
- (2013) Laetitia Dubau et al. APPLIED CATALYSIS B-ENVIRONMENTAL
- An identical-location transmission electron microscopy study on the degradation of Pt/C nanoparticles under oxidizing, reducing and neutral atmosphere
- (2013) L. Dubau et al. ELECTROCHIMICA ACTA
- Probing Degradation by IL-TEM: The Influence of Stress Test Conditions on the Degradation Mechanism
- (2013) Alessandro Zana et al. JOURNAL OF THE ELECTROCHEMICAL SOCIETY
- Dissolution of Platinum: Limits for the Deployment of Electrochemical Energy Conversion?
- (2012) Angel A. Topalov et al. ANGEWANDTE CHEMIE-INTERNATIONAL EDITION
- Stability investigations of electrocatalysts on the nanoscale
- (2012) Josef C. Meier et al. Energy & Environmental Science
- Evidences of the migration of Pt crystallites on high surface area carbon supports in the presence of reducing molecules
- (2012) Z. Zhao et al. JOURNAL OF POWER SOURCES
- Carbon corrosion and platinum nanoparticles ripening under open circuit potential conditions
- (2012) Z. Zhao et al. JOURNAL OF POWER SOURCES
- Electrocatalyst approaches and challenges for automotive fuel cells
- (2012) Mark K. Debe NATURE
- Model- and Theory-Based Evaluation of Pt Dissolution for Supported Pt Nanoparticle Distributions under Potential Cycling
- (2011) Steven G. Rinaldo et al. ELECTROCHEMICAL AND SOLID STATE LETTERS
- An EC-FTIR study on the catalytic role of Pt in carbon corrosion
- (2011) F. Maillard et al. ELECTROCHEMISTRY COMMUNICATIONS
- The effect of platinum on carbon corrosion behavior in polymer electrolyte fuel cells
- (2011) Nicolas Linse et al. ELECTROCHIMICA ACTA
- Further insights into the durability of Pt3Co/C electrocatalysts: Formation of “hollow” Pt nanoparticles induced by the Kirkendall effect
- (2011) L. Dubau et al. ELECTROCHIMICA ACTA
- Identical-location TEM investigations of Pt/C electrocatalyst degradation at elevated temperatures
- (2011) Katrin Schlögl et al. JOURNAL OF ELECTROANALYTICAL CHEMISTRY
- Identical locations transmission electron microscopy study of Pt/C electrocatalyst degradation during oxygen reduction reaction
- (2011) Francisco J. Perez-Alonso et al. JOURNAL OF POWER SOURCES
- Surface oxidation of carbon supports due to potential cycling under PEM fuel cell conditions
- (2010) Bharat Avasarala et al. ELECTROCHIMICA ACTA
- Nanoscale compositional changes and modification of the surface reactivity of Pt3Co/C nanoparticles during proton-exchange membrane fuel cell operation
- (2010) L. Dubau et al. ELECTROCHIMICA ACTA
- Durability of Pt[sub 3]Co/C Cathodes in a 16 Cell PEMFC Stack: Macro/Microstructural Changes and Degradation Mechanisms
- (2010) L. Dubau et al. JOURNAL OF THE ELECTROCHEMICAL SOCIETY
- Impact of ultra-low Pt loadings on the performance of anode/cathode in a proton-exchange membrane fuel cell
- (2009) E. Billy et al. JOURNAL OF POWER SOURCES
- Fuel cell catalyst degradation on the nanoscale
- (2008) Karl J.J. Mayrhofer et al. ELECTROCHEMISTRY COMMUNICATIONS
- Non-destructive transmission electron microscopy study of catalyst degradation under electrochemical treatment
- (2008) Karl J.J. Mayrhofer et al. JOURNAL OF POWER SOURCES
- Carbon support oxidation in PEM fuel cell cathodes
- (2007) S. Maass et al. JOURNAL OF POWER SOURCES
Find Funding. Review Successful Grants.
Explore over 25,000 new funding opportunities and over 6,000,000 successful grants.
ExploreBecome a Peeref-certified reviewer
The Peeref Institute provides free reviewer training that teaches the core competencies of the academic peer review process.
Get Started