期刊
WEAR
卷 289, 期 -, 页码 46-57出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.wear.2012.04.016
关键词
Slurry erosion; Thermal spray coatings; Steel; Erosion testing; Surface analysis
资金
- All India Council for Technical Education (AICTE), New Delhi [8023/BOR/RID/RPS-128/2007-08]
Hydroturbine components generally suffer from severe wear due to slurry erosion caused by solid particles entrained in the flowing water. High-velocity oxy-fuel (HVOF) spray process is known for depositing protective coatings on the materials. In this work, WC-10Co-4Cr and Al2O3+13TiO(2) coatings were deposited on CF8M turbine steel by HVOF spray process and studied with regard to their performance under slurry erosion conditions. High speed erosion test rig was used for slurry erosion tests and effect of three parameters namely average particle size, speed (rpm) and slurry concentration on slurry erosion of these materials was investigated. The bare steel and Al2O3+13TiO(2) coating followed ductile and brittle mechanisms respectively under slurry erosion, whereas the WC-10Co-4Cr coating exhibited mixed behaviour (mainly ductile). WC-10Co-4Cr coating was found to be useful to increase the slurry erosion resistance of steel remarkably. (C) 2012 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据