TiN coating; Vacuum cold spray; Electrical property; Microhardness; Fracture toughness; Porosity
Titanium nitride (TiN) coatings were fabricated by vacuum cold spray (VCS) process at room temperature with nano-sized starting powder (about 20 nm in size). The microstructure of the powder and coating was examined by scanning electron microscope and X-ray diffraction. The porosity and pore distribution of the VCS TIN coatings were measured by the N-2 adsorption-desorption method. The microhardness and fracture toughness of the coatings were evaluated by using the micro-indentation technique. The sheet resistance and electrical resistivity of the coatings were characterized by the four-point probe method. The results show that the sheet resistance of coatings is significantly reduced from 13565 to 127 Omega with increasing the coating thickness. A minimum electrical resistivity of 1.8 x 10(-3) Omega m is achieved. The VCS TiN coatings with high porosity ranging from 58.3 to 67.6% exhibit low hardness of 279-490 HV and relatively good fracture toughness of about 3.12 MPa m(1/2). (C) 2011 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据