期刊
TRIBOLOGY TRANSACTIONS
卷 54, 期 3, 页码 417-423出版社
TAYLOR & FRANCIS INC
DOI: 10.1080/10402004.2011.553027
关键词
Fabric; Solid Lubricants; Friction; Wear
资金
- National Project 973 [2007 CB607601]
- Fund for Creative Research Groups [50721062]
- National Natural Science Foundation [50773089]
Hybrid polytetrafluoroethylene (PTFE)/Nomex (DuPont, USA) composite specimens were prepared with graphite and MoS2 as fillers. The friction and wear tests were conducted under dry sliding conditions at a speed of 0.26 m/s under various loads and environmental temperatures. The results showed that the incorporation of graphite was effective in reducing the wear of the hybrid PTFE/Nomex fabric composite, whereas the MoS2 filler was unfavorable for improving the wear resistance. X-ray photoelectron spectroscopy (XPS) results revealed that MoS2 was oxidized into MoO3 during sliding. The absence of the layered structure of MoO3 resulted in a higher wear rate of fabric composite. Differential scanning calorimetry (DSC) analysis of unfilled and graphite-filled composites and their debris indicated that graphite increased the thermal stability of the unfilled composite and therefore enhanced the wear resistance.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据