TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA
卷 23, 期 12, 页码 3822-3828出版社
ELSEVIER
DOI: 10.1016/S1003-6326(13)62935-0
关键词
cyanide-free silver electroplating; thiosulfate; current density; bonding strength; grain size
资金
- National Natural Science Foundation of China [50771042]
- Program for Science and Technology Innovation Talents of Henan Province, China [104100510005, 2009HASTIT023]
Cyanide-free silver electroplating was conducted in thiosulfate baths containing AgNO3 and AgBr major salts, respectively. The effects of major salt content and current density on surface quality, deposition rate and microhardness of Ag coatings were investigated. The optimized electroplating parameters were established. The adhesion strength of Ag coating on Cu substrate was evaluated and the grain size of Ag coating was measured under optimized electroplating parameters. The optimized AgNO3 content is 40 g/L with current density of 0.25 A/dm(2). The deposited bright, smooth, and well adhered Ag coating had nanocrystalline grains with mean size of 35 nm. The optimized AgBr content was 30 g/L with current density of 0.20 A/dm(2). The resultant Ag coating had nanocrystalline grains with mean size of 55 nm. Compared with the bath containing AgBr main salt, the bath containing AgNO3 main salt had a wider current density range, and corresponding Ag coating had a higher microhardness and a smaller grain size.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据