Rapid and controlled electrochemical synthesis of crystalline niobium oxide microcones

We demonstrate the fabrication by anodization of niobium oxide microcones, several microns long, from aqueous solutions of 1 wt% hydrogen fluoride (HF) with varied sodium fluoride (NaF) concentration (0-1 M). Raman spectroscopy and x-ray diffractometer analysis revealed the as-grown microcones to be crystalline Nb2O5-x with preferred (1 0 0) and (0 1 0) orientations. The overall Nb2O5-x formation rate increased with the increasing NaF concentration, and structures as tall as 20 mu m were achieved in just 20 min of anodization at 1 M NaF. Rapid formation of niobia microcones was even observed in the absence of HF at this NaF concentration. Photocatalytic activity for water oxidation was highest for microcones grown under the highest NaF concentration.