SYNTHETIC METALS
卷 160, 期 7-8, 页码 701-707出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.synthmet.2010.01.004
关键词
Polypyrrole; Polypyrrole base; Polyaniline; Cerium(IV) sulfate; Conducting polymer
资金
- Ministry of Education of the Slovak Republic
- Slovak Academy of Sciences [2/0064/10, 1/0774/08]
- Academy of Sciences of the Czech Republic [IAA 400500905]
- Czech Grant Agency [202/08/0686]
The conducting polymers, polypyrrole and polyaniline, were synthesized by chemical oxidative polymerization of the corresponding monomers in 0.1 M sulfuric acid using cerium(IV) sulfate as the oxidant at mole ratios of oxidant-to-monomer ranging from 0.5 to 3. The yields of the oxidation products were determined, and the sample were characterized with respect to their elemental composition, molecular structure, and morphology. The conductivity of polypyrrole prepared in 0.1 M sulfuric acid, 10(-1) to 10(0) S cm(-1), was higher compared with the conductivity of polyaniline prepared under the same conditions, 10(-3) to 10(-1) Scm(-1). The loss of mass after deprotonation with ammonium hydroxide is reported, and discussed in terms of the type of protonation as also reflected by FTIR spectroscopy. The conductivity of polypyrrole bases remained at relatively high level, 10(-5) to 10(-3) S cm(-1), while PANI bases became non-conducting, 10(-12) to 10(-1) S cm(-1). The polymers had a granular morphology in all cases. (C) 2010 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据