期刊
SURFACE & COATINGS TECHNOLOGY
卷 252, 期 -, 页码 35-47出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.surfcoat.2014.04.062
关键词
AA2024 alloy; EIS; Anodization; XPS; Raman spectroscopy; Sealing of anodized layer
资金
- CSIR Supra Project [SIP-00-01]
In the present study sulphuric acid anodized oxide layer was sealed with permanganate (MnO) and permanganate-vanadate (MnVO) ions. The effect of the incorporation of these oxyanions on the corrosion performance of plain oxide layer (PO) was investigated by various characterization techniques such as field emission scanning electron microscopy (FESEM), energy dispersive X-ray analysis (EDAX), atomic force microscopy (AFM), X-ray photoelectron spectroscopy (XPS) and Raman spectroscopy. The barrier layer resistance value of plain oxide layer was increased about 13 times due to the incorporation of mixed Mn-V oxyanions. The damage function (D) calculations revealed the self-healing mechanism of MnVO. The potentiodynamic polarization results showed higher corrosion inhibition performance of MnVO compared to that of MnO even after 336 h of immersion in 3.5% (0.6 M) NaCl solution. No sign of visible corrosion products were observed on MnVO surface even after 2000 h of continuous salt spray exposure. (C) 2014 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据