关键词
Coatings; Carbides; TRD; AISI 1045; Niobium; Corrosion
Niobium carbide coatings were deposited on AISI 1045 low alloy steel via the thermo-reactive deposition/diffusion technique (TRD). The influence of the percentage of the ferroalloy on the corrosion resistance of each coating was evaluated. The corrosion resistance of the niobium carbide coatings was evaluated using potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) in a solution of 3.0% NaCl. The microstructure was characterized via X-ray diffraction (XRD), and the morphology was characterized by means of scanning electron microscopy (SEM). Chemical analysis of the layers was done through Energy dispersive X-ray spectroscopy (EDS) and X-ray photoelectron spectroscopy (XPS). The results show that the thickness of the carbide coatings does not significantly change with an increasing amount of ferroalloy. Carbide coatings improved the corrosion resistance of the substrates; however, the corrosion resistance of these layers decreased after 24 h of being exposed to the saline solution used, due to the porosity of the coatings and the roughness of the coating-substrate interface. For the most part, the results of the tests of corrosion resistance were not affected by the percentage of ferroalloy in the salt bath. (C) 2014 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据