期刊
SURFACE & COATINGS TECHNOLOGY
卷 235, 期 -, 页码 735-740出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.surfcoat.2013.08.059
关键词
DLC; AISI 420; Adhesion; Tribology
DLC films have a high hardness, extremely low friction coefficient, and they are chemically inert Plasma nitriding can serve as a pre-treatment to increase adhesion and improve tribological performance of the DLC coating. In this work, the mechanical and tribological behaviour of a DLC film deposited on martensitic stainless steel is studied. Two different surface finishing techniques were accomplished before the nitriding process: paper grinding and polishing with diamond powder. Plasma nitriding was carried out in a DC pulsed discharge, and the DLC film was deposited by Plasma Assisted CVD. The nitrided layer and film were observed with an optical microscope and SEM. The tribological behaviour was analysed in sliding wear tests and adhesion was tested. The coating was 3 mu m thick, and the nitrided layers were about 11 mu m in the polished samples and only 8 mu m in the grounded ones. The coated samples yielded a better wear resistance than the pre-nitrided samples but only on the polished nitrided samples did the film present an acceptable adhesion. (C) 2013 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据