SURFACE & COATINGS TECHNOLOGY
卷 213, 期 -, 页码 192-201出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.surfcoat.2012.10.046
关键词
Silica film; Magnesium alloy; Micro-arc oxidation; Sol-gel; Corrosion resistance
资金
- National Ministry of Science and Technology [2009AA033501]
- National Natural Science Foundation of China [50971089]
To improve the corrosion resistance, a superhydrophobic silica film on Mg-3.0Nd-0.2Zn-0.4Zr (wt.%, NZ30K) magnesium alloy was successfully prepared by the combination of micro-arc oxidation (MAO) and sol-gel method using tetraethoxysilane (TEOS) and methyltriethoxysilane (MTES) as precursors. The MAO layer with highly porous surface was formed as an intermediate layer to ensure the excellent adhesion of superhydrophobic silica film to the substrate. The parameters of the sol-gel process such as molar ratios of TEOS/C2H5OH and MTES/TEOS had significant effects on the surface morphologies and water-repellent properties of the silica films. A superhydrophobic silica film with static contact angle of 151 degrees was obtained as the molar ratios of TEOS/C2H5OH and MTES/TEOS were 1/30 and 1/2 respectively. It is shown that the superhydrophobic silica film can significantly improve the corrosion resistance of NZ30K magnesium alloy by nearly three orders of magnitude by analysis of the potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) tests in 3.5 wt.% NaCl solution. 168 h immersion test further demonstrates that the superhydrophobic silica film can effectively provide long-term corrosion protection for NZ30K magnesium alloy. In addition, the superior corrosion protection performance of the superhydrophobic silica film compared with that of the pure silica film without the addition of MTES can be attributed to the good coverage of hydrophobic methyl groups on its surface, which could effectively decrease the direct contact surface to corrosive medium. (C) 2012 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据