STEEL RESEARCH INTERNATIONAL
卷 82, 期 4, 页码 337-345出版社
WILEY-BLACKWELL
DOI: 10.1002/srin.201000118
关键词
austenitic stainless steels; deformation-induced martensitic transformation; electron backscattered diffraction (EBSD); spontaneous martensitic transformation
资金
- VINNOVA
- Swedish Government Agency for Innovation Systems
- Swedish Industry
- KTH (Royal Institute of Technology)
The fraction and microstructure of spontaneous and deformation-induced martensite in three austenitic stainless steels with different austenite stability have been investigated. Samples were quenched in brine followed by cooling in liquid nitrogen or plastically deformed by uniaxial tensile testing at different initial temperatures. In-situ ferritescope measurements of the martensite fraction was conducted during tensile testing and complemented with ex-situ X-ray diffractometry. The microstructures of quenched and deformed samples were examined using light optical microscopy and electron backscattered diffraction. It was found that annealing twins in austenite are effective nucleation sites for spontaneous alpha'-martensite, while deformation-induced alpha'-martensite mainly formed within parallel shear-bands. The alpha'-martensite formed has an orientation relationship near the Kurdjumov-Sachs (K-S) relation with the parent austenite phase even at high plastic strains, and adjacent alpha'-martensite variants were mainly twin related (< 111 > 60 degrees or Sigma 3).
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据