期刊
STEEL RESEARCH INTERNATIONAL
卷 81, 期 4, 页码 292-298出版社
WILEY-BLACKWELL
DOI: 10.1002/srin.201000008
关键词
Hot Press Forming; Hot Stamping; Martensite; Phase Transformations
In the present study, the aluminized 22MnB5 Hot Press Forming (HPF) steel was deformed isothermally in the temperature range of 600-800 degrees C. The specimens were deformed with 0%, 10% and 30% engineering strain at a strain rate of 0.5/s. Mechanical stabilization of austenite during phase transformation was observed. The influence of strain rate was also studied. It was found that the martensite transformation was affected by the combined effect of mechanical stabilization and dynamic recovery The influence of high temperature deformation on the final microstructure, microhardness and mechanical properties were studied. Deformation applied below 750 degrees C resulted in a significant decrease of the strength and the hardness. The ferrite fraction and morphology had a clear effect on the room temperature tensile fracture morphology.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据