期刊
SOLID STATE SCIENCES
卷 12, 期 11, 页码 1857-1860出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.solidstatesciences.2010.01.019
关键词
Tungsten oxide; Hexagonal; Monoclinic; Gas sensor; Selectivity; H2S
资金
- Hungarian National Research Fund [OTKA T-049131]
- Agency for Research Fund Management [KPI-EU-GVOP-3 2 1 -2004-04-0224/3 0 KMA]
Hexagonal and monoclinic tungsten oxide (h- and m-WO3) samples were produced by annealing hexagonal ammonium tungsten bronze (NH4)(0) (07)(NH3)(0) (04)(H2O)(0) 09WO2 (95) at 470 and at 600 C respectively Their structure composition and morphology were analyzed by XRD Raman XPS H-1-MAS NMR and SEM In order to study the effect of crystal structure on the gas sensitivity of tungsten oxides h- and m-WO3 were tested as gas sensors to CH4 CO H-2 NO and H2S (1000 and 10 ppm) at 200 C Monoclinic WO3 responded to all gases but its gas sensing signal was two magnitudes greater to 10 ppm H2S than to other gases and it also detected H2S even at 25 degrees C Hexagonal WO3 responded only to 10 ppm H2S Its sensitivity was smaller compared to m-WO3 however the response time of h-WO3 was significantly faster The gas sensing tests showed that while m-WO3 had relative selectivity to H2S in the presence CH4 CO H-2 NO h-WO3 had absolute selectivity to H2S in the presence these gases (C) 2010 Elsevier Masson SAS All rights reserved
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据