期刊
SENSORS AND ACTUATORS B-CHEMICAL
卷 195, 期 -, 页码 446-451出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.snb.2013.12.120
关键词
SAW sensors; Humidity sensors; ZnO nanorods; Ga-doped ZnO
资金
- Vietnam National Foundation for Science and Technology Development (NAFOSTED) [103.02-2011.33]
- Excellence Program in the school of Electrical Engineering at University of Ulsan
ZnO nanorods were grown on a Si/AlN structure using hydrothermal method. The fabricated ZnO nanorod film was used as a sensitive material layer for surface acoustic wave (SAW) humidity sensor. The concentration of gallium, which was doped into ZnO seed layers prior to ZnO nanorod chemical growth, varied from 0 wt% to 3 wt% to control ZnO nanorod growth. The result shows that gallium dopant was crucial for controllable dimension of ZnO nanorods. ZnO nanorod length increased and ZnO nanorod diameter decreased when Ga concentration increased from 0 wt% to 3 wt%. The ZnO nanorods had a hexagonal wurtzite structure, and were aligned vertically on the substrate. SAW properties (e.g., resonance frequency) over relative humidity (RH) ranging from 10% to 90% at room temperature were investigated. The results show that the frequency shift of the SAW humidity sensors increased with increasing Ga dopant concentration. The largest shift in the frequency response was approximately 970 kHz at 90% RH for sensors with ZnO nanorods grown on 3 wt% Ga-doped ZnO seed layer. This result was caused by the highest surface-to-volume ratio of the ZnO nanorod sensing layer. (C) 2014 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据