A two-parameter model to predict fatigue life of high-strength steels in a very high cycle fatigue regime
出版年份 2015 全文链接
标题
A two-parameter model to predict fatigue life of high-strength steels in a very high cycle fatigue regime
作者
关键词
Very high-cycle fatigue, High-strength steels, Fatigue life, Inclusion size, Crack growth rate
出版物
ACTA MECHANICA SINICA
Volume 31, Issue 3, Pages 383-391
出版商
Springer Nature
发表日期
2015-05-27
DOI
10.1007/s10409-015-0451-4
参考文献
相关参考文献
注意:仅列出部分参考文献,下载原文获取全部文献信息。- Effects of stress ratio on high-cycle and very-high-cycle fatigue behavior of a Ti–6Al–4V alloy
- (2015) Xiaolong Liu et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Experimental study on very high cycle fatigue of martensitic steel of 2Cr13 under corrosive environment
- (2014) S. X. Li et al. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- A fracture mechanics approach to interior fatigue crack growth in the very high cycle regime
- (2013) Takeshi Ogawa et al. ENGINEERING FRACTURE MECHANICS
- Effect of submillimeter size holes on the fatigue limit of a high strength tool steel
- (2013) A. Shyam et al. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- Defect size dependence on threshold stress intensity for high-strength steel with internal hydrogen
- (2013) Y. Murakami et al. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- Influence of mean stress and variable amplitude loading on the fatigue behaviour of a high-strength steel in VHCF regime
- (2013) M. Sander et al. INTERNATIONAL JOURNAL OF FATIGUE
- Propensities of crack interior initiation and early growth for very-high-cycle fatigue of high strength steels
- (2013) Youshi Hong et al. INTERNATIONAL JOURNAL OF FATIGUE
- Effects of stress ratio on crack growth rate and fatigue strength for high cycle and very-high-cycle fatigue of metallic materials
- (2013) Chengqi Sun et al. MECHANICS OF MATERIALS
- Very-High-Cycle-Fatigue of in-service air-engine blades, compressor and turbine
- (2013) A. A. Shanyavskiy Science China-Physics Mechanics & Astronomy
- Effects of loading condition on very-high-cycle fatigue behaviour and dominant variable analysis
- (2013) ZhengQiang Lei et al. Science China-Physics Mechanics & Astronomy
- A rapid scatter prediction method for very high cycle fatigue
- (2012) Z. Y. HUANG et al. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- A cumulative damage model for fatigue life estimation of high-strength steels in high-cycle and very-high-cycle fatigue regimes
- (2012) C. SUN et al. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- Effects of inclusion size and stress ratio on fatigue strength for high-strength steels with fish-eye mode failure
- (2012) Chengqi Sun et al. INTERNATIONAL JOURNAL OF FATIGUE
- Gigacycle fatigue behaviors of two SNCM439 steels with different tensile strengths
- (2011) Zheng Duan et al. ACTA MECHANICA SINICA
- Prediction of threshold value for FGA formation
- (2011) Aiguo Zhao et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Fatigue Strength and Crack Initiation Mechanism of Very-High-Cycle Fatigue for Low Alloy Steels
- (2011) Youshi Hong et al. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE
- Prediction of the S–N curves of high-strength steels in the very high cycle fatigue regime
- (2010) Y.B. Liu et al. INTERNATIONAL JOURNAL OF FATIGUE
- Fatigue crack initiation detection by an infrared thermography method
- (2009) D. WAGNER et al. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- Reliability evaluation on very high cycle fatigue property of GCr15 bearing steel
- (2009) W. Li et al. INTERNATIONAL JOURNAL OF FATIGUE
- Effect of loading condition on very high cycle fatigue behavior in a high strength steel
- (2009) Masaki Nakajima et al. INTERNATIONAL JOURNAL OF FATIGUE
- Similitude and the Paris crack growth law
- (2008) R JONES et al. INTERNATIONAL JOURNAL OF FATIGUE
- Fatigue crack growth from small to large cracks on very high cycle fatigue with fish-eye failures
- (2007) Israel Marines-Garcia et al. ENGINEERING FRACTURE MECHANICS
- Estimation of the size of GBF area on fracture surface for high strength steels in very high cycle fatigue regime
- (2007) Z YANG et al. INTERNATIONAL JOURNAL OF FATIGUE
Find Funding. Review Successful Grants.
Explore over 25,000 new funding opportunities and over 6,000,000 successful grants.
ExploreDiscover Peeref hubs
Discuss science. Find collaborators. Network.
Join a conversation