SCIENCE AND TECHNOLOGY OF WELDING AND JOINING
卷 18, 期 7, 页码 566-572出版社
TAYLOR & FRANCIS LTD
DOI: 10.1179/1362171813Y.0000000136
关键词
Hot cracking; Crater crack; Alloy 52M; ER308L; CF8A; Slope down time
Effects of ER308L buffer layer and welding parameter slope down time on the hot cracking susceptibility of alloy 52M overlay on CF8A base metal were studied. The results indicated that Si segregation was a critical factor affecting Alloy 52M hot cracking. Applying ER308L buffer layers between CF8A and Alloy 52M can reduce the dilution of Alloy 52M weld beads and minimise the contribution of Si from CF8A into Alloy 52M, thereby alleviating Si segregation and the hot cracking susceptibility of Alloy 52M. When the Si content in the grain boundary region was lower than 0.81 wt-%, the hot cracking in the weld bead could be mitigated completely. In many cases, crater cracks occurred in the end crater of the weld bead. Increasing the number of ER308L buffer layers and extending the slope down time could reduce crater crack susceptibility. However, the Si content in the grain boundary region should be controlled to be lower than 0.63 wt-% to prevent crater cracking.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据