PROTECTION OF METALS AND PHYSICAL CHEMISTRY OF SURFACES
卷 45, 期 5, 页码 588-594出版社
MAIK NAUKA/INTERPERIODICA/SPRINGER
DOI: 10.1134/S2070205109050165
关键词
-
资金
- Collaborative Call with Moldova INTAS program [15-104-7540]
- National Scientific Foundation of the United States [0231279]
- Fulbright stipend
The relation between the composition, morphology, and corrosion resistance of the electrolytic CoMoP coatings plated at various current densities from citrate baths containing ammonia or hydrazine and various amounts of sodium hypophosphite is studied. Phosphorus was included in the coatings as a result of the electrochemical reduction of hypophosphite ions. Ternary Co-Mo-P alloys containing up to 26 at % Mo and up to 3 at % P were electroplated. Coatings of the highest quality were obtained from a bath containing hydrazine admixture at a temperature of 50A degrees C. Corrosion resistance of CoMoP coatings increases with an increase in the Mo content and a certain decrease in the phosphorus amount in the deposit. The best protective properties were demonstrated by coatings obtained at higher concentrations of sodium hypophosphite and high deposition current densities when CoMoP alloys containing 23 +/- 2 at % Mo and up to 1.5 at % P were formed.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据