Mg-Y; Corrosion; Microstructure
资金
- National Key Technology R&D Program of China [2011BAE22B01, 2011BAE22B06]
- Beijing Engineering Research Center for Advanced Manufacturing and Evaluation of Special Vehicle Parts
The corrosion behavior of Mg-(0.25, 2.5, 5, 8 and 15)Y alloys in 3.5wt.% NaCl aqueous solution was investigated. It was found that the degree of corrosion deterioration increased with increasing immersion time up to 2 h. Corrosion modes for the alloys with low and high content of Y element were general corrosion and pitting corrosion, respectively, and the threshold content for the corrosion mode change was 2.5 A for the tested alloys. The experimental results showed that the addition of Y refined the grain of the alloy, and the distribution, i.e., continuous or not, of the Mg24Y5 phases had great effect on the corrosion rate and corrosion mode. (C) 2012. Chinese Materials Research Society. Production and hosting by Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据