Ultrafine-grained; High-strength; Powder metallurgy; Mg-3Al-Zn alloys
资金
- Scientific and Technological Project of Heilongjiang [DCQQ24404018]
Mg-3Al-Zn alloys with ultrafine grain size (UFG) have been fabricated by consolidation of ball milling nanocrystalline powders. Firstly, the elemental powders of Mg, Al and Zn were ball milled to synthesize nanocrystalline alloy powders. The milled powders stored in an Al container were sintered for 40 min at 633 K in a vacuum furnace. The sintered samples were extruded at the temperature range from 373 to 573 K for further densification. The bulk alloys with an average grain size of 180 nm showed a yield stress of 379 MPa, which was two times higher than that of the coarse-grained AZ31, and their ultimate strength was 417 MPa with a 5% elongation. The high strength of the alloys was attributed to three strengthening mechanism: the fine grain strengthening, dispersion strengthening and solid solution strengthening. Low strain hardening was observed in the UFG alloy, which may be caused by room temperature dynamic recovery during plastic deformation. (C) 2011 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据