期刊
POLYMER DEGRADATION AND STABILITY
卷 98, 期 1, 页码 348-355出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.polymdegradstab.2012.09.014
关键词
Polylactide; Clay; Nanocomposites; Degradation; Gamma irradiation
资金
- EGIDE through the TASSILI program
The oxidative degradation of neat polylactide (PLA) and PLA-Cloisite 30B (DOB) nanocomposites under gamma irradiation was studied for irradiation doses ranging from 0 to 200 kGy. The morphologies and the properties of neat PLA and PLA-C30B nanocomposites (5 wt.%) were investigated using Fourier transform infrared spectroscopy (FT-IR), size exclusion chromatography (SEC), differential scanning calorimetry (DSC), thermogravimetric analysis (ATG), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and nanoindentation measurements. The results were analysed by comparing the C30B influence on the PLA degradation. Results show neat PLA is strongly degraded by gamma irradiation while PLA-C30B nanocomposites are less affected because gamma irradiation promotes the DOB layer distribution within the PLA matrix. The morphological defects were much less more pronounced for the PLA nanocomposites compared to neat PLA, for which many voids and cracks were observed after irradiation. (C) 2012 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据