POLYMER DEGRADATION AND STABILITY
卷 95, 期 9, 页码 1557-1567出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.polymdegradstab.2010.06.009
关键词
Polypropylene; Poly(ethylene oxide); Titanium dioxide; Calcium phosphate; Degradation
资金
- Japan Society for the Promotion of Science [22510097]
- Grants-in-Aid for Scientific Research [22510097] Funding Source: KAKEN
To prepare a novel photo-degradable polypropylene (PP) with a higher degradation rate, a PP composite containing a poly(ethylene oxide) (PEO)/modified TiO2 microcapsule was prepared. The modification of the TiO2 was performed by the synthesis of octacalcium phosphate intercalated with succinic acid ion (OCPC) under various Ca/P molar ratio conditions. It was found that the synthesis conditions of the Ca/P = 3.5 and 3.6 M ratios were suitable to prepare the OCPC. However, the microscopic composition on the TiO2 surface was different between these Ca/P conditions and affected the PP photo-degradation rate in the PP/PEO/modified TiO2 composite. It was found from the Fourier Transform Infrared (IR) and the tensile testing measurements that the existence of the OCPC covering material on the TiO2 surface brought about the higher PP photo-degradation rate. The facilitation behavior of the degradation was due to the release of the acid species (succinic acid ion) from the OCPC in the degradation process. In addition, the higher coverage of the OCPC on the TiO2 surface brought about an induction period for the degradation. (C) 2010 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据