POLYMER DEGRADATION AND STABILITY
卷 93, 期 8, 页码 1433-1437出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.polymdegradstab.2008.05.020
关键词
poly(3-hydroxybutyrate); thermal degradation; kinetics; beta-elimination; unzipping reaction; crotonic acid
资金
- Ministry of Higher Education, Malaysia
The thermal degradation of poly(3-hydroxybutyrate) (PHB) was investigated by kinetic analyses in detail to clarify its complex degradation behavior, resulting in a finding of mixed mechanisms comprising at least a thermal random degradation with subsequent auto-accelerated transesterification, and a kinetically favored chain reaction from crotonate chain ends. The thermal degradation behavior of PHB varied with changes in time and/or temperature. From the kinetic analysis of changes in molecular weight, it was found that a non-auto-catalytic random degradation proceeding in the initial period was followed by an auto-accelerated reaction in the middle period. From the kinetic analysis of weight loss behavior, it is proposed that there are some kinetically favored scissions occurring at the chain ends, where the degradation proceeded by a 0th-order weight loss process in the middle stage. The observed 0th-order weight loss process was assumed to be an unzipping reaction occurring at ester groups neighboring the crotonate end groups. (C) 2008 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据