A new type of organophilic clay grafted with the protonated 4, 4'-methylenediamine was prepared. The epoxy was modified using the organophilic clay and was prepared by acetone-clay slurry method. The morphology of the clay platelets into epoxy matrix were characterized by wide angle X-ray diffraction and transmission electron microscopy. The results indicated that the epoxy resin/exfoliated clay hybrid materials were successfully prepared and the exfoliation of clay into epoxy matrix occurred in the curing process. The excellent thermal mechanical properties of the hybrid materials with the values of the storage modulus and glass transition temperature (T.) of the hybrid materials were studied by dynamic mechanical analysis. When 7 wt% of modified clay was added into epoxy, the storage modulus of hybrid materials increased to 1131 MPa at 110 degrees C, and 51 MPa at 220 degrees C in comparison to the pristine cured epoxy (661 MPa at 110 degrees C and 6 MPa at 220 degrees C). The high thermal stabilities of the hybrid materials especially in high temperature were also been researched by thermogravimetric analysis. POLYM. COMPOS., 30:948-954, 2009. (C) 2008 Society of Plastics Engineers
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据