卷 54, 期 12, 页码 2958-2965出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.polymer.2013.04.011
关键词
In-chain multi-functionalized polymer; 1,1-Bis(4-dimethylaminophenyl)ethylene; Dispersed polymer composite filler
资金
- National Natural Science Foundation of China [NSFC 21034001]
In-chain multi-functionalized polystyrene possessing definite geminal dimethylamino groups along the polymer backbone, poly(styrene-co-1,1-bis(4-dimethylaminophenyl)ethylene) (poly(styrene-co-BDADPE)), has been designed and synthesized via living anionic copolymerization of styrene with 1,1-bis(4-dimethylanimophenyl)ethylene in benzene at 50 degrees C, using sec-butyllithium as initiator. The amine functionality was readily controlled by the monomer feed ratio and molecular weight. Compositions of styrene/BDADPE were 9.0-57.9 when ratios of styrene/BDADPE = 0.45-7.79 and Mn = 4.7 -15.5 kg/mol. The incorporation of 1,1-bis(4-dimethylanimophenyl)ethylene unit resulted in an increase in glass transition temperature of copolymer and was hindered in the presence of Lewis base. The monomer reactivity ratio for styrene, r(1) = 53.4, was obtained. Such in-chain multi-functionalized polystyrene significantly improved the dispersity of carbon black in the corresponding composites, as verified by SEM observation. This in-chain multi-functionalization of matrix polymer via anionic copolymerization employing 1,1-bis(4-dimethylaminophenyl)ethylene as comonomer provides a facile and effective method to prepare carbon black-based polymer composites with good dispersity. (c) 2013 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据