期刊
POLYMER
卷 49, 期 18, 页码 3973-3978出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.polymer.2008.07.006
关键词
crystalline-crystalline diblock copolymers; organic semiconductors; polythiophene
资金
- European Synchrotron Radiation Facility (ESRF), Grenoble, France
We report on the development of the solid-state structure from the melt of crystalline-crystalline diblock copolymers consisting of the semiconducting poly(3-hexylthiophene) (P3HT) and insulating polyethylene (PE) - a material combination that previously was shown to feature promising characteristics for applications in flexible organic electronics. The nature of the structures obtained from the melt was found to generally be dictated by crystallization of the PE block, which solidified after the P3HT sequence. This resulted in the formation of classical spherulitic structures for diblock copolymers of low P3HT content. At P3HT contents exceeding 10-20 wt%, the semiconductor block increasingly hampered crystallization of the PE moiety, with the P3HT entity arranging into columnar and at higher content into lamellar micelle-type domains. Unlike the rate of crystal growth of the two moieties, interestingly, the dimensionality of both entities of the diblock copolymers was found to be unaffected by the presence of the dissimilar block. Crown Copyright (C) 2008 Published by Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据