Fabrication of highly ordered, macroporous Na2W4O13 arrays by spray pyrolysis using polystyrene colloidal crystals as templates

Highly ordered, macropore arrays, that is, inverse opal structures, of Na2W4O13 were successfully synthesized by spray pyrolysis using polystyrene ( PS) colloidal crystals as templates. A densely packed monolayer of monodisperse PS microspheres was deposited on a silica glass substrate by use of the Langmuir-Blodgett thin film technique. Subsequently, Na2W4O13 layers were deposited on the PS templates as a thin layer by spray pyrolysis of a 5(NH4)(2)O center dot 12WO(3)center dot 5H(2)O-NaCl solution. The PS templates were, finally, removed by thermal treatment, generating a surface with features ( inverse opal structures) located where the interstitial space of the densely hexagonal-packed PS microspheres had been. The macroporous structures obviously depended on the annealing conditions such as time and temperature. The macropores were basically hemispherical in shape and highly honeycombed arrangement, which corresponded well to the PS templates. The inverse opal textures of Na2W4O13 layer surfaces enhanced their hydrophobicity. The surfaces modified by fluoroalkylsilane (FAS) were converted from hydrophobic (water contact angle = 127 degrees) to hydrophilic (30 degrees) by photocatalytic oxidation using the Na2W4O13 crystal layer. The Na2W4O13 crystals exhibited high activity for FAS photodegradation.