PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS
卷 468, 期 15-20, 页码 1404-1407出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.physc.2008.05.122
关键词
REBa2Cu3Oy; bulk; microstructure; critical current density
We have investigated the relationship between microstructure and pinning properties of Y123 melt-solidified bulks having systematically controlled oxygen contents. The subgrain structure was developed along crystal growth direction in the a-growth region. while it was not observed in the c-growth region. The formation of such subgrains could be explained by an elastic property of the edge dislocations and RE123 crystal growth process. Through evaluations on the second peak effects of J(c)-B curves and irreversibility fields, it was found that Y123/Y211 interfaces do not act as the predominant pinning centers under high fields against the reported theoretical predictions. Furthermore, our results suggested that the precipitation of Y211 particles decreases J(c) in high fields. The resulting pinning properties of Y123 melt-solidified bulks were discussed in relationship to the subgrain structure. (C) 2008 Published by Elsevier B.V.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据