期刊
OPTICAL MATERIALS
卷 34, 期 5, 页码 893-900出版社
ELSEVIER
DOI: 10.1016/j.optmat.2011.11.027
关键词
Y2O3 thin films; Crystal structure; Morphology; Band gap; Optical constants
Yttrium oxide (Y2O3) thin films were grown onto Si(100) substrates using reactive magnetron sputter-deposition at temperatures ranging from room temperature (RT) to 500 degrees C. The effect of growth temperature (T-s) on the growth behavior, microstructure and optical properties of Y2O3 films was investigated. The structural studies employing reflection high-energy electron diffraction RHEED indicate that the films grown at room temperature (RT) are amorphous while the films grown at T-s = 300-500 degrees C are nanocrystalline and crystallize in cubic structure. Grain-size (L) increases from similar to 15 to 40 nm with increasing T-s. Spectroscopic ellipsometry measurements indicate that the size-effects and ultra-microstructure were significant on the optical constants and their dispersion profiles of Y2O3 films. A significant enhancement in the index of refraction (n) (from 2.03 to 2.25) is observed in well-defined Y2O3 nanocrystalline films compared to that of amorphous Y2O3. The observed changes in the optical constants were explained on the basis of increased packing density and crystallinity of the films with increasing T-s. The spectrophotometry analysis indicates the direct nature of the band gap (E-g) in Y2O3 films. E-g values vary in the range of 5.91-6.15 eV for Y2O3 films grown in the range of RT-500 degrees C, where the lower E-g values for films grown at lower temperature is attributed to incomplete oxidation and formation of chemical defects. A direct, linear relationship between microstructure and optical parameters found for Y2O3 films suggest that tuning optical properties for desired applications can be achieved by controlling the size and structure at the nanoscale dimensions. (c) 2011 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据