期刊
MICROPOROUS AND MESOPOROUS MATERIALS
卷 151, 期 -, 页码 34-43出版社
ELSEVIER
DOI: 10.1016/j.micromeso.2011.11.019
关键词
Acidity; Aluminosilica; Ordered mesoporous silica; Hydroisomerization
类别
资金
- NWO-ACTS
- NWO-NSC
- NWO
To increase the content of well-dispersed aluminum in Al/SBA-15 and its Bronsted acidity, a water-free synthesis method involving a Si-O-Al precursor was employed to prepare a series of Al/SBA-15 of widely varying composition. The materials were characterized with ICP, BET, TEM, Al-27 MAS NMR and IR spectroscopy and compared to conventionally prepared Al/SBA-15. For low Al content (Si/Al > 10), the conventional approach leads to highly dispersed, predominantly isolated Al with well-ordered mesopores. At higher Al content, the order decreased or was even completely lost. In general, this led to the agglomeration of Al species on the surface. Although in most cases a substantial part of Al atoms exhibit tetrahedral coordination indicating their high dispersion and interaction with the silica, the overall Bronsted acidity of these Al/SBA-15-type materials is very low. The overall acidity of all Al/SBA-15 is of the same order as amorphous silica-alumina. By IR spectroscopy of H/D exchange with perdeuterobenzene, it was found that the intrinsic acidity of the acid sites in Al/SBA-15 is similar to that in zeolites and amorphous silica-alumina, thus further confirming that acid site concentration dominates differences in acidity of aluminosilicas. (c) 2011 Elsevier Inc. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据