MATERIALS TRANSACTIONS
卷 52, 期 6, 页码 1096-1103出版社
JAPAN INST METALS & MATERIALS
DOI: 10.2320/matertrans.MC201007
关键词
magnesium alloy; long-period stacking ordered (LPSO) phase; mechanical property; 14H-typed structure; 18R-typed structure; deformation
资金
- Japan Science and Technology Agency
- Ministry of Education, Culture, Sports, Science and Technology of Japan
We investigated the influence of a change in the stacking sequence of the close-packed plane in a Mg12ZnY long-period stacking ordered (LPSO) phase on its mechanical properties. A 14H-typed LPSO-phase crystal was fabricated by annealing a directionally solidified (DS) crystal with a 18R-typed LPSO-structure at 525 degrees C for 3 days, and the temperature dependence and orientation dependence of the yield stress were examined via compression tests. (0001)< 11 (2) over bar0 > basal slip was identified as a dominant deformation mode, and deformation kink bands were formed under compression in the case of suppression of basal slip motion. The deformation mechanism of the 14H-typed LPSO-phase is almost similar to that of the 18R-typed LPSO-phase, even though a slight difference was observed at temperatures above 300 degrees C. [doi:10.2320/matertrans.MC201007]
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据