MATERIALS SCIENCE AND ENGINEERING B-ADVANCED FUNCTIONAL SOLID-STATE MATERIALS
卷 157, 期 1-3, 页码 53-57出版社
ELSEVIER
DOI: 10.1016/j.mseb.2008.12.008
关键词
Mumetal; Nanocrystalline; Magnetic properties; Mechanical alloying
资金
- Nanyang Technological University
Ni-Fe based alloy powders are interesting materials for their application as soft magnetic material with low coercivity and high permeability. In this study, nanocrystalline Ni0.77Fe0.16Cu0.05Cr0.02 (Mumetal)alloy powders were synthesized by mechanical alloying process using planetary high-energy ball mill under argon atmosphere. The alloy formation and different physical properties were studied as a function of milling time (h), ranging from Oh to 96h, using X-ray diffraction (XRD) technique, scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDS) and the vibrating sample magnetometer (VSM). The complete phase formation of gamma-(Fe, Ni, Cu, Cr) is observed after 12 h milling time. Powder morphology at different stages was examined by SEM and different particle shape was observed. Saturation magnetization and coercivity derived from the hysteresis curves are discussed as a function of milling time and showed that saturation magnetization increases and coercivity decreases with milling time. Increase in milling time, led to reduction in crystallite size (D) and increase in lattice parameter (a), thus inducing a higher magnetization and lower coercitivity. (C) 2008 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据