Fatigue; Short fatigue cracks; Fatigue micromechanics; Al-Si; Fatigue; Piston alloys
类别
资金
- Faculty of Engineering and the Environment of the University of Southampton
- University of Nairobi
The short fatigue crack growth behaviour of a model cast aluminium piston alloy has been investigated. This has been achieved using a combination of fatigue crack replication methods at various intervals during fatigue testing and post-mortem analysis of the crack profiles. Crack-microstructure interactions have been clearly delineated using a combination of optical microscopy and scanning electron microscopy. Results show that intermetallic particles and eutectic Al-Si regions play a significant role in determining the crack path and growth rate of short fatigue cracks. It is observed that the growth of short cracks is often retarded or even arrested at intermetallic particles and Al-Si eutectic regions. Crack deflection at intermetallics and eutectic Si is also frequently observed. These results have been compared with the long crack growth behaviour of the alloy. (C) 2014 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据