Tensile fracture and thermal conductivity characterization of toughened epoxy/CNT nanocomposites

Rubber toughened epoxy/CNT nanocomposites were manufactured at different weight percents between 0 and 1% of multiwall carbon nanotube (MWNT) using a high intensity ultrasonic liquid processor with a titanium probe. Mechanical properties of manufactured dog bone samples were measured in tension and the results indicated a maximum of 23% increase in the elastic modulus at 0.6% by weight of MWNT. However, the fracture strength showed a maximum decrease of about 11% as a function of increasing MWNT loading. Scanning Electron Microscopy (SEM) images from the neat samples revealed a distinct circular pit at the top left edge of the specimen with an overall tearing deformation causing the fracture paths. Comparatively, all nanocomposite samples on an average seemed to show a prominent brittle fracture with little or no evidence of circular pit formation. The amount of tearing deformation seemed to be enhanced in the nanocomposite specimens as compare to the neat ones. Finally, Transmission Electron Microscopy images indicated that different states of dispersion exist in all of the nanocomposite samples. The data showed that agglomeration of nanotubes increases as a function of weight percent. In addition to mechanical property characterization, thermal conductivity of all the samples was determined as a function of temperature between 30 degrees C and 100 degrees C using the 3 omega method. The tested samples showed an almost 16% increase in thermal conductivity. The minimal enhancement in thermal conductivity has been analyzed from the standpoint of the Effective Medium Theory. Interfacial thermal resistances exhibit no order of magnitude changes explaining the conductivity results. (C) 2010 Elsevier B.V. All rights reserved.